ASTM B571 PDF

ASTM B Standard Practice for Qualitative Adhesion Testing of Metallic Coatings. standard by ASTM International, 08/01/ View all product details. ASTM B quantifies various physical properties of metal coating substances such as gold, copper, silver and several others on their adhesion quality via. ASTM B STANDARD PRACTICE FOR QUALITATIVE ADHESION TESTING OF METALLIC COATINGS_建筑/土木_工程科技_专业资料。.

Author: Kajikree Brazil
Country: Fiji
Language: English (Spanish)
Genre: Technology
Published (Last): 11 January 2016
Pages: 248
PDF File Size: 12.80 Mb
ePub File Size: 19.15 Mb
ISBN: 694-1-89332-856-4
Downloads: 81454
Price: Free* [*Free Regsitration Required]
Uploader: Dinos

We offer machines, apparatus, testers, tensile grips, test fixtures, clamps, holders, jigs, faces, jaws, extensometers, environmental and humidity chambers, furnaces, baths and custom solutions for unique applications. These tests have varying degrees of severity; and one might serve to distinguish between satisfactory and unsatisfactory adhesion in a specific application. These tests have varying degrees of severity; and one might serve to distinguish between satisfactory and unsatisfactory adhesion in a speci?

Exfoliation or blisters in and around indentations are evidence of inadequate adhesion.

ASTM B Adhesion Metals Coating Test Equipment

We are confident that we have what you are looking for. If you feel that your comments have not received a fair hearing you should make your views known to the ASTM Committee on Standards, at the address shown below.

The choice for each situation must be determined. If the deposited coating cannot be peeled or lifted from the substrate in an area adjacent to the blister sthe appearance of blisters should not be interpreted as evidence of inferior adhesion.

Examine the region at low magni? This test is commonly used if the coating will peel without tearing. Last previous edition approved in as B — 97 This would not give a correct indication of the as-plated bond strength.

  CS 400RGY PDF

Supporting the material on a ring about 2. A suitable tool is a steel rod 6 mm in diameter with a smooth hemispherical end. ASTM B quantifies various physical properties of metal coating substances such as gold, copper, silver and several others on their adhesion quality via various methods for quality standards comparisons.

Work Item s – proposed revisions of this standard.

ASTM B571 Adhesion Metals Coating Test Equipment

Historical Version s – view previous versions of standard. If there is peeling or?

Vol 22,p. If more than one test is used, failure to pass any one test is considered unsatisfactory. Then quench the part in water or other suitable liquid at room temperature. Current edition approved April 1, The mandrel diameter should be four times the thickness of the sample.

If any portion of coating between the lines breaks away from the substrate, the adhesion is inadequate. This may be prying, hammering, bending, beating, heating, sawing, grinding, pulling, scribing, chiseling, or a combination of such treatments.

The adhesion is not adequate if the tape has deposit adhering to it that comes from the area between the scribed lines. The tape shall be wide enough to cover three or more parallel lines of the scribed area.

ASTM B This test practice is a simple set of tests to determine the adhesion of metallic coatings on various substances. Such adhesion is usually obtained if good electroplating practices are followed. Have a question about conducting the test for this standard?

  KINEMATIC FACEBOW PDF

Blisters may erupt during the heat and quench test when plating solution is entrapped in substrate surface pits or pores which are bridged by the deposit. Examine the deformed area visually under low magni? Precision and Bias Such cracks may or may not propagate into the substrate. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

Deposit continuous to the scribed lines is not considered.

Your comments are invited either for revision of this standard or for additional standards and should be addressed to ASTM International Headquarters. In scribing the lines, use sufficient pressure to cut through the coating to the substrate in a single stroke.

If the coating peels, flakes, or lifts from the substrate, the adhesion is less than perfect. The pressure shall be sufficient to burnish the coating at each stroke but zstm so great as to dig into it.

Soft and ductile coatings are generally not suited for evaluation. Such adhesion is usually obtained if good electroplating practices are followed.

Because the results of tests in cases of marginal adhesion are subject to interpretation, agreement shall be reached on what is acceptable. The standard describes several different tests and tables to compare different metallic coatings for a given application.